fig9
![Hot isostatic pressing induced precipitation strengthening at room and high temperature of <InlineParagraph>Ni-Fe-Cr-Al-V</InlineParagraph> high-entropy alloy manufactured by laser powder bed fusion](https://image.oaes.cc/1d2c3be1-4eaa-450f-9c4f-c27b24e8081f/microstructures3065.fig.9.jpg)
Figure 9. Engineering stress-strain curves and corresponding work hardening rate curves of LPBF-processed and HIP-processed Ni-Fe-Cr-Al-V HEAs tested at (A and B) 293 K, (C and D) 773 K and (E and F) 1,173 K, respectively.
Figure 9. Engineering stress-strain curves and corresponding work hardening rate curves of LPBF-processed and HIP-processed Ni-Fe-Cr-Al-V HEAs tested at (A and B) 293 K, (C and D) 773 K and (E and F) 1,173 K, respectively.