fig8
![Hot isostatic pressing induced precipitation strengthening at room and high temperature of <InlineParagraph>Ni-Fe-Cr-Al-V</InlineParagraph> high-entropy alloy manufactured by laser powder bed fusion](https://image.oaes.cc/1d2c3be1-4eaa-450f-9c4f-c27b24e8081f/microstructures3065.fig.8.jpg)
Figure 8. TEM micrographs of the microstructure in HIP-processed Ni-Fe-Cr-Al-V HEA: (A) BF-TEM image and SAED pattern of B2 precipitates, (B) EDS maps of B2 phases, (C) DF-TEM image and SAED pattern of L12 precipitates and (D) EDS maps of L12 precipitates.