fig9
![A review on high-throughput development of high-entropy alloys by combinatorial methods](https://image.oaes.cc/3ccd8edd-e976-4817-b25f-14f584ee2607/5493.fig.9.jpg)
Figure 9. (A) Fractions of CALPHAD predicted single-phase solid solution, intermetallics, and solid solution and intermetallic equimolar alloys in 3 to 6 component alloy systems at the melting temperature (Tm) and at 600 °C. This figure is quoted with permission from Senkov et al.[130]; (B) two-dimensional projection of AlaCrbMocNbdTieV1-a-b-c-d-e phase diagram from CALPHAD showing compositions within two-dimensional space where a BCC solid solution phase forms at 800K. This figure is quoted with permission from Klaver et al.[131]. IM: Intermetallic; SS: solid solution.