Figure 6. Microstructure and defects of refractory HEAs fabricated by L-PBF: (A) NbMoTa; (B) NbMoTaTi; (C) NbMoTaTi0.5Ni0.5. (D) Compressive strength of as-printed NbMoTaTi0.5Ni0.5 at various temperatures[67].