Figure 4. Hierarchical microstructure and tensile properties of FeCoCrNiMn HEA fabricated by L-PBF: (A) inverse pole figure mapping of as-printed sample along the building direction; (B) bright-field scanning transmission electron microscopy (BF-STEM) image of cellular structure with corresponding SAED pattern; (C) engineering stress-strain curves of as-printed and as-cast samples (“V2000” and “V2500” represent the scanning speed of the laser with values of 2000 and 2500 mm/s, respectively)[59].