fig4

Figure 4. Electrochemical characterization of a cell containing the 57% NMC₉₅₅+ 38% Li₆PS₅Cl+3% C₆₅+2% SBR cathode with active material Li⁰/Li₆PS₅Cl/NMC₉₅₅. (A and B) PEIS and cyclic voltammetry analysis of the cell before the electrochemical cycling; (C) best electrochemical cycles for each C-rate; (D) cycles at C/10, C/5 and C; (E and F) Specific capacity vs. cycle number for charge and discharge, respectively, for the following C-rates: C/50, C/20, C/10, C/5, C/3, C/2, C, C/10, 2C, 3C, C/10, C/5, C/3, C/2, and C; (G and H) PEIS and cyclic voltammetry analysis of the cell after the electrochemical cycling. Cells tested at 25 C with no applied pressure; areal capacity of the cathode: 0.167 mAh.cm^-2. Note: In E the lowest charging C-rate at CV varies from C/15 to C/76 for an average of C/46 and in F the lowest discharging average C-rate at CV is C/24. The maximum discharge capacity at C C-rate is > 120 mAh.g^-1. SBR: Styrene-butadiene rubber; PEIS: potentiostatic electrochemical impedance spectroscopy; CV: constant voltage.