fig5
![Binary anion and cation co-doping enhance sulfide solid electrolyte performance for all-solid-state lithium batteries](https://image.oaes.cc/986d73a5-d595-4d17-a2dd-614336ed225d/em4078.fig.5.jpg)
Figure 5. Lithium plating/stripping voltage profiles of (A) Li/LPS/Li, (B) Li/LPS-0.05SiO2/Li, (C) Li/LPS-0.05GeO2/Li, and (D) Li/LPS-0.05SnO2/Li cells at different current densities.
Figure 5. Lithium plating/stripping voltage profiles of (A) Li/LPS/Li, (B) Li/LPS-0.05SiO2/Li, (C) Li/LPS-0.05GeO2/Li, and (D) Li/LPS-0.05SnO2/Li cells at different current densities.