fig7
![Quasi-solid-state electrolytes - strategy towards stabilising Li|inorganic solid electrolyte interfaces in solid-state Li metal batteries](https://image.oaes.cc/7a51a42f-906c-4abd-bd6e-0e8984716874/5603.fig.7.jpg)
Figure 7. (A) Schematic diagram of the role of IL interlayer between bulk LAGP and Li along with SEM images at low-magnification (a) and high-magnification (b) and cross sectional SEM images in low-magnification (c) and high-magnification (d) of cycled Li anode with LAGP-ILE interlayer. Lithium stripping/plating analysis showing interfacial stability of bulk LAGP pellet and Li anode with the presence of IL, and charge-discharge performance and rate capability of solid-state Li|LAGP |LiFePO4 full cells with and without ILE interlayer. This figure is quoted with permission from Xiong et al.[148]. (B) Li stripping/plating voltage profiles of symmetric Li|LLZO|Li cells with and without ILE conducted at 25 °C. This figure is quoted with permission from Pervez et al. This figure is quoted with permission from