Crystal facet engineering of electrocatalysts for nitrate reduction to ammonia: recent advances and future perspectives
Abstract
Ammonia (NH3) is an important chemical feedstock and a clean energy carrier that has a pivotal impact on the sustainable energy circle. Its electrocatalytic production is evolving into a green alternative to the traditional Haber-Bosch process. A key strategy in enhancing the performance of this electrocatalytic ammonia synthesis is crystal facet engineering of electrocatalysts, which could significantly influence the reaction mechanism, kinetics, and thermodynamics. This review summarizes the recent advancements in crystal facet engineering for electrocatalytic nitrate reduction to ammonia. Through this review, we hope to shed light on the significant role of crystal facet engineering in advancing electrocatalytic ammonia production and provide useful guidance on the design of high-performance electrocatalysts.
Keywords
INTRODUCTION
Ammonia (NH3), as a key chemical in numerous industrial applications, has widespread usage as a primary raw material in manufacturing fertilizers[1], explosives, refrigerants, and pharmaceuticals. About 50% of the nitrogen content in the human body comes from synthetic ammonia, indicating that ammonia is crucial to human beings and the global economy. Additionally, as a carbon-free energy carrier, ammonia possesses a high energy density of 3 kWh·kg-1. It serves as a viable option for direct liquid fuel utilization in electricity and power generation applications. This can be achieved by using direct ammonia fuel cells or catalytic ammonia combustion methods. Ammonia also can be used to store hydrogen with a high hydrogen capacity of 17.75 wt%[2]. Compared to hydrogen, it can be easily liquefied when compressed to 1 MPa at room temperature (298 K) or cooled to 240 K at ambient pressure (0.1 MPa), making it an ideal medium for the safe transportation and storage of hydrogen[3,4].
The global ammonia production is currently 170 million tonnes per year[5], mostly coming from the Haber Bosch process (N2 + H2 → NH3) that typically requires high temperatures (400-500 °C) and pressures (15-
However, the large-scale application of NtrRR still faces many challenges, such as high overpotential and low Faraday efficiency and ammonia yield, which are mostly associated with efficiency of the electrocatalysts. Therefore, many strategies, such as nanostructuring[13], doping[7,14,15], and alloying[16-18], have been explored to enhance the performance of electrocatalysts. Among them, crystal facet engineering is regarded as a highly effective approach since the crystal facet represents the most fundamental element of a nanostructure. It directly determines the surface atomic arrangement and orientation and, therefore, the adsorption and activation of the reactants and intermediates, which essentially determine the catalytic activity. Indeed, crystal facet engineering has shown the efficacy of enhancing the electrocatalyst performance towards not only the NtrRR but also many other electrocatalytic reactions, including HER, NRR, oxygen reduction reaction (ORR), and oxygen evolution reaction (OER)[19-21]. It is well acknowledged that high-index facets generally possess higher catalytic activity; however, they are thermodynamically unstable and, thus, are difficult to synthesize through common methods. While low-index facets, on the other hand, are much easier to synthesize, they could still significantly influence both the activity and stability of the catalysts. Therefore, understanding the relationship between the crystal facets and NtrRR performance is essential for the rational design of high-performance electrocatalysts.
In this review, we summarize the recent advances in crystal facet engineering of electrocatalysts for the NtrRR, focusing on the effects of different facets on the reaction mechanism, kinetics, and thermodynamics. We also discuss the challenges and opportunities in this research field and provide some perspectives for future development.
REACTION MECHANISM OF NtrRR
Electrocatalytic nitrate reduction reaction is a complex multi-electron and multi-proton transfer process, and the final product exists in the form of chemically stable N2 [Equation (1)] and/or NH3 [Equation (2)]:
Depending on the specific conditions and catalysts, the reaction can follow either an indirect or a direct pathway[22,23]. The indirect pathway only occurs under conditions of NO3- concentration greater than
In addition, the adsorbed NO3 can also be reduced by the adsorbed *H that is generated by water dissociation through the Volmer process [Equation (6)][24]. The *H then participates in the reduction of intermediates (NO3-, *NO2-, and *NO) to *N [Equations (7)-(9)]. This process is known as *H-mediated reduction, distinguished from the electron-mediated reduction discussed earlier. The *H-mediated process would preferably form *NH3 as *H-mediated N–H bonds are easier to form than N–N bonds [Equations (10)-(12)]. *NH3 then desorbs from the electrode surface to produce NH3.
Resulting from the complex multi-electron coupled proton transfer process, NtrRR suffers from sluggish kinetics and low selectivity towards NH3. The NtrRR performance highly depends on the properties of electrocatalysts, which determine the adsorption and activation of reactants and intermediates. Tremendous efforts have, therefore, been devoted to exploring efficient and stable electrocatalysts to promote the reaction kinetics and selectivity. Crystal facet engineering has emerged as a successful approach to boost the performance of electrocatalysts in various electrochemical reactions, including the HER, NRR[25-27], and ORR[19,20]. This is because the crystal facets determine the atomic configurations and, thus, the interactions between the surface active sites and reaction intermediates, resulting in improved reaction energetics.
CRYSTAL FACETS AND REGULATION STRATEGIES
A crystal facet is a plane that passes through any three points of the spatial lattice of a crystal, and it is denoted by the Miller index (hkl). Figure 2A shows a triangle diagram that illustrates the direct relationship between the shapes of polyhedra and the corresponding facets in a cubic crystal system[28]. The vertices of the triangle symbolize three common polyhedra enclosed by low-index facets: a cube with six (100) facets, an octahedron with eight (111) facets, and a rhombic dodecahedron with twelve (110) facets. The coordination numbers of the atoms on the outermost layer of the (111), (100), and (110) facets are 9, 8, and 7, respectively. The other crystal facets are referred to as high-index facets (h, k, l having at least one greater than 1). The edges of the triangle [(001), (110), (011) crystal zones] and its interior represent different facets. These facets correspond to four types of high-index facet polyhedra: tetrahexahedron (THH), trapezohedron (TPH), trisoctahedron (TOH), and hexoctahedron (HOH). Each polyhedron is characterized by various small facets that are closely associated with its specific shape. For instance, the THH polyhedron consists of 24 (hkl) facets, where h, k, and l are integers and follow the condition h > k > l = 0. Similarly, the TPH polyhedron possesses 24 (hkl) facets with the condition h > k = l > 0. The TOH polyhedron has 24 (hkl) facets satisfying the condition h = k > l > 0, and the HOH polyhedron is composed of 48 (hkl) facets wherein h > k > l > 0[29]. Low-index facets, such as Ag (100), (111), (110) and Pt (111) facets, are flat surfaces at the atomic level, with densely packed surface atoms [Figure 2B]. While high-index facets, such as Ag (211), Pt (311) and (211), have rough surfaces with atomic steps. They often possess high surface energies and, thus, are more active for chemical reactions[30,31].
Figure 2. (A) Relationship between the shape of a crystal and its facets. Reproduced with permission[28]. Copyright 2010, American Chemical Society; (B) Surface atomic arrangement of Ag (100), (111), (110), (211) and Pt (311), (211) facets. Reproduced with permission[30,31]. Copyright 2015 and 2020, American Chemical Society; (C) Growth rates of specific facets determine the exposed surfaces.
Understanding the growth behavior is the prerequisite for regulating the crystal facets. The crystal shape is determined by the growth rates of its facets. According to the crystal growth law[32], facets with slower growth rates occupy a larger fraction of the crystal surface than those with faster growth rates. This is illustrated in Figure 2C, where the dihedral angles between facets M and N are constant throughout the growth process, as dictated by the law of conservation of crystal plane angles. If facet M grows slower than facet N, then facet N will gradually shrink or vanish as the crystal grows, leaving facet M as the dominant surface. Conversely, if facet M grows faster than facet N, then facet N will become the dominant surface. Therefore, regulating the growth rates of crystal facets is crucial for exposing specific surfaces.
High-index facets are highly reactive and challenging to stabilize due to their thermodynamic instability. The synthetic methods that have been developed encompass wet chemistry, electrochemistry, and solid-state chemistry synthesis.
Currently, most high-index facet nanocrystals are synthesized using the wet chemistry method, which has the advantage of easy large-scale synthesis. Numerous studies have incorporated surfactants, polymers, capping agents, small molecules, ions, etc., into the synthesis process. These additives could adsorb onto specific crystal facets and slow the growth rate (adsorption-mediated route), enabling the synthesis of nanocrystals with various crystal facet exposures. For instance, Yang et al. synthesized cyclic penta-twinned Rh icosahedral nanocrystals using a one-pot hydrothermal method in the presence of a capping agent
Figure 3. (A) Diagram of synthesizing Rh nanocrystals of different shapes in different solvents. Reproduced with permission[33]. Copyright 2018, Springer Nature; (B) Schematic diagram of the kinetically controlled overgrowth (when V2 is much larger than V1) of concave nanocubes evolved from pseudo-nanocubes. Reproduced with permission[34]. Copyright 2014, Royal Society of Chemistry; (C) SEM images of Cu2O polyhedra synthesized with different concentrations of NaOH. Reproduced with permission[35]. Copyright 2012, The Royal Society of Chemistry; (D) SEM images of Pt (311), (111) and (100). The inset presents size histogram and atomic model of the facet. Reproduced with permission[36]. Copyright 2023, OAE Publishing Inc; (E) Scheme for synthesizing THH particles. Reproduced with permission[37]. Copyright 2019, American Association for the Advancement of Science. SEM: Scanning electron microscopy; THH: tetrahexahedron.
However, the morphology control agents (typically organic molecules) are challenging to remove during the wet chemistry synthesis process, often impeding the catalytic activity. Consequently, the synthesis of high-index facet nanocrystals with clean surfaces primarily follows the electrochemical method. This technique, however, also has limitations in scaling up and in the universal preparation of nanocrystals. Electrochemical synthesis is predominantly based on the square-wave potential (SWP) method, which induces periodic oxygen adsorption and desorption. Over the past decade, various metal nanocrystals with different high-index facets and compositions have been synthesized using electrochemical SWP methods. For example, Hu et al. prepared trapezohedral Pt nanocrystals surrounded by (311) high-index facets on a glassy carbon electrode using the electrochemical SWP method [TPH Pt-(311)][36]. The surface structures of the prepared Pt nanocrystals were investigated by cyclic voltammetry scanning. The oxygen adsorption currents in the oxygen species adsorption and desorption regions were significantly larger for TPH Pt-(311) than for Pt (111) and Pt (100) [Figure 3D]. This is primarily due to the preferential adsorption of oxygen atoms onto the step atoms with lower coordination numbers, suggesting that the TPH Pt-(311) surface has a higher density of step atoms.
Foreign metals can alter the surface energy of nanocrystals. Therefore, the deposition of foreign metals on metal nanocrystals by underpotential deposition (UPD) can obstruct specific crystal facets (UPD-mediated route), enabling the nanocrystal synthesis with different crystal facet exposures. Huang et al. prepared THH nanocrystals of Pt, Pd, Rh, Ni, Co, and bimetallic particles by solid-state chemistry, with sizes ranging from 10 to 500 nm [Figure 3E][37]. The solid metal precursors were heated in a tube furnace, where the nanoparticle growth was influenced by an atmosphere containing foreign metals (Sb, Bi, Pb, and Te). In this process, an alloy is initially formed and then de-alloyed by evaporating the heterogeneous metals at higher temperatures, forming a THH nanocrystal primarily surrounded by (210) facets.
In summary, synthesizing different crystal facets and exposing various step atoms can not only change the intrinsic activity of the catalyst, accelerate the electron transfer and optimize the adsorption of intermediates, but also change the active site, which can greatly optimize the performance if there are more intermediate stations of electron transfer with the reactant intermediates. Similarly, in the field of electrocatalytic NtrRR, we will discuss how the crystal facets would affect the NtrRR performance below.
ELECTROCATALYSTS WITH SPECIFIC LOW-INDEX FACETS FOR THE NtrRR
Noble metal electrocatalysts
Noble metals have been identified as highly active electrocatalysts for NtrRR. They crystallize in a cubic crystal system, and the regulation of crystal facets is relatively easy. Many researchers have investigated the influence of crystal facets on the selectivity and activity of NtrRR, aiming to further optimize the catalytic performance. Han et al. synthesized Pd cubes, octahedra, and rhombic dodecahedra with exposed (100), (111), and (110) facets using a simple seed-mediated method [Figure 4A][38]. In neutral conditions, Pd (111), (110), and (100) crystal facets were tested for NH3 yield, Faraday efficiency, and selectivity. The Pd (111) yielded 0.5485 mmol·h-1·cm-2 NH3, with a Faraday efficiency of 79.91% and an NH3 selectivity of 77.26%, along with excellent durability for 20 h of electrolysis. Density functional theory (DFT) calculations indicated that NO3- tends to adsorb more on the Pd (111) surface, exhibiting lower HER activity, which benefits the NtrRR. Since the NtrRR involves various intermediates, and different crystal facets exhibit varying interaction behavior with these intermediates, the performance of the electrocatalysts might be further boosted by combining diverse facets. For instance, Lim et al. synthesize Pd nanoparticles with controlled crystal facets, including Pd nanocubes with exposed (100) facets, octahedra with (111) facets, cubic octahedra with (100) and (111) facets, concave nanocubes with (100), and high-index (hk0) facets
Figure 4. Noble metal electrocatalysts with low-index facets for the NtrRR. (A) NH3 yield rates and Faraday efficiencies of Pd (111), (110), and (100) facets (left panel). Free energy diagram for NtrRR (middle) and the reaction energies of H2 formation (right) over Pd (111), (110), and (100) facets. Reproduced with permission[38]. Copyright 2021, Elsevier; (B) NH3 yield rates and Faraday efficiencies of Pd catalysts with different shapes (left panel). Adsorption energy of NO3- (middle) or NO2- (right) at pH = 0 and the activation barrier for converting *NO3 to *NO2 and *NO2 to *NO. Reproduced with permission[39]. Copyright 2021, American Chemical Society; (C) Surface configurations of nitrate adsorption on Rh (111), (110), and (100) facets. Reproduced with permission[40]. Copyright 2021, Elsevier; (D) Diagrammatic representation of the low coordination Rh atoms (left panel) and the NH3 yield rate of Rh nanoparticles and nanoflowers (right). Reproduced with permission[41]. Copyright 2023, American Chemical Society; (E) Schematic illustration of the reversible redox-transitions on Pt surface. Reproduced with permission[43]. Copyright 2023, Elsevier.
In a similar vein, Guo et al. employed DFT calculations to predict the NtrRR energetics on the Rh (111) (110) and (100) facets [Figure 4C] by investigating the surface adsorption of five major species (NO2, NO, N2O, N2, and NH3) involved in NtrRR[40]. The findings suggest that the exposed facets of Ru substantially influence the energetics of the NRR (NtrRR). Among the different facets studied, Rh (100) showed the highest level of activity for ammonia production. Furthermore, the optimal potential range for achieving efficient NtrRR on Rh (100) was identified to be between 0.15-0.09 V vs. RHE. They further conducted the experiments to verify the calculation results, and a peak NH3 yield of 34.4 μg·h-1·cm-2 was achieved. However, the Faraday efficiency turned out to be unexpectedly low (20.8%). Interestingly, Liu et al. demonstrated Rh nanoflowers with the (111) facet as the main exposed surface exhibit decent NtrRR performance with a high Faraday efficiency of 95% at the potential of 0.2 V vs. RHE [Figure 4D][41]. In addition, the required overpotential of the Rh nanoflowers was also much lower than most catalysts reported so far. The contradictory results from these two studies indicate that the role of crystal facets might be more complex and require further investigation. X-ray absorption spectroscopy analysis suggested that Rh nanoflowers have abundant low coordination Rh atoms. DFT calculations further revealed that these atoms can enhance the adsorption of NO3- and better stabilize reaction intermediates, therefore resulting in superior NtrRR performance.
Among all noble metals, Pt is perhaps the most extensively studied electrocatalyst for the NtrRR because of its strong electrocatalytic performance and excellent reduction effectiveness. Katsounaros et al. analyzed the NtrRR energetics on Pt (111) and (100) in an acidic nitrate electrolyte[42]. They discovered that *NO is a key intermediate and could poison the Pt surface. They further demonstrated that only Pt (111) could achieve the complete conversion of NO3- to NH3 in a narrow potential window. This behavior, however, could significantly differ in alkaline electrolytes. Molodkina et al. demonstrated that among all Pt facets, the Pt (100) facet exhibits the highest activity in the reduction of NO3- and NO. In contrast, the Pt (111) facet shows structural sensitivity in the reduction of NO3- and NO, with incomplete reduction of NO on Pt (111)[43]. They found that *NO occupies two different types of sites on the Pt (111) surface: atop and 3-fold hollow. *NO adsorbed on atop surface sites is reduced to form *NH3 and stabilized by adsorption on hollow sites. The produced ammonia does not detach but creates co-adsorption compounds with adjacent NO molecules bound to hollow sites, which are supported by dipole-dipole interactions and hydrogen bonding. Upon affecting the reduction degree of the adsorbed layer by the *NO, the *NO/*NH3 complexes start to decompose. Due to this, hydrogen adatoms formed in the respective range of potentials cause the adsorption of NH3 on the surface to weaken. As long as no further reduction occurs and the electrode remains within the potential range in which hollow-bound NO molecules are not reduced, co-adsorption complexes are expected to remain stable. In these circumstances, there is a transition from hydrofluoric acid to hydrogen chloride at potentials around 0.6 V. Although the hydrogen bonds may become less strong due to the degradation of the hydrofluoric acid, the strong dipole-dipole interactions stabilize the complex. Relativistic 1.1 V conditions result in reversible oxidation of atop-bound NO species to nitrite species (HNO2). Conversely, hollow-bound NO species do not oxidize when co-adsorption is formed with *NH2. As a result, no NO to HNO2 redox transition occurs [Figure 4E].
Non-noble metal electrocatalysts
While noble metal electrocatalysts show good NtrRR performance, their high cost limits the large-scale application. Considerable endeavors have thus been dedicated to investigating alternative catalysts based on non-noble metals. Among them, Cu-based materials are the most widely studied. The relatively large hydrogen adsorption free energy (ΔGH) on these materials can inhibit the competitive HER. Moreover, their d-orbital energy levels are similar to the LUMO π* of NO3-, making them good electrocatalysts towards the NtrRR. Hu et al. used DFT to calculate the pathway of NtrRR on Cu (111), (100), and (110) facets at different pH values [Figure 5A][44]. There was a significant pH effect on the catalytic hydrogenation and deoxygenation processes. Further study showed that pH was also a factor for rate control steps and overpotential. In addition, pH value changes can also affect the competition between HER and NtrRR. Through studying the NH3 generation from NtrRR and HER on different crystal facets, it was found that Cu (100) and (111) facets contribute the most to the NtrRR, while Cu (110) contributes the least. In particular, in near-neutral and alkaline environments, Cu (111) is most effective, whereas Cu (100) is most effective in strongly acidic environments. According to the author, the local coordination environment and the electronic states of surface atoms are responsible for the different NtrRR levels towards NH3 production on the Cu surface. Due to the stereospecificity of Cu-Cu pairs, strong *NOH adsorption and weak *NH3 adsorption were achieved on Cu (111) and (100), thereby promoting the NtrRR. To further improve the catalytic performance of Cu-based materials with a single crystal facet, Fu et al. developed Cu nanosheets derived in situ from CuO nanosheets for NtrRR [Figure 5B][45]. In situ electrochemical spectroscopy determined which phases were catalytically active in the prepared CuO nanosheets. The Cu K-edge X-ray absorption near edge structure (XANES) spectra of the CuO nanosheet electrocatalyst prepared at open circuit potential (OCP) were similar to the reference CuO, indicating their resemblance in absorption edges. However, applying NtrRR current caused a shift in the spectra of the CuO nanosheet towards the reference Cu foil, suggesting an electrochemical reduction of the CuO nanosheets to metallic Cu in situ. The outstanding performance of the electrocatalyst was ascribed to the synergistic effect between the Cu (100) and (111) facets, as confirmed by electrochemical tests and DFT calculations. The presence of Cu (100) facilitated the generation of NO2-, which was subsequently hydrogenated on the Cu (111) facet, promoting the hydrogenation of *NO to *NOH through a relay catalysis mechanism. The Cu nanosheet catalyst has a current density of 665 mA·cm-2 at -0.59 V vs. RHE, an NH3 yield of 1.41 mmol·h-1·cm-2, a Faraday efficiency of 88%, and a high stability for 700 h at 365 mA·cm-2. In addition, Hu et al. developed an electrocatalyst synthesis strategy based on in situ electrochemical reduction of copper oxide nanoribbons under NtrRR conditions [Figure 5C][46], which effectively exposed the Cu (100) surface with abundant surface defects that significantly promoted the generation of NtrRR and effectively suppressed HER. Impressively, in alkaline media, the yield of NH3 catalyzed by defective Cu (100) surface is 2.3 times higher than that generated through the Haber Bosch process. They demonstrated using *N as a capping agent to regulate the exposed surface while carrying out the reduction process. The upward shift of the d-band center of copper, brought about by the synergistic effect of Cu (100) crystal facet and defects, holds the key to attaining outstanding performance.
Figure 5. Cu-based electrocatalysts with low-index facets for the NtrRR. (A) Surface structures of Cu (111), (100), and (110) (left panel), NtrRR mechanism on Cu (111) (middle), and the ΔG for different facets at different pH (right). Reproduced with permission[44]. Copyright 2021, American Chemical Society; (B) Tandem interaction of Cu (100) and (111) facets (left panel). In situ Cu K-edge XANES and EXAFS spectra of CuO nanosheets under various conditions (right). Reproduced with permission[45]. Copyright 2023, Wiley Online Library; (C) Graphical depiction of NtrRR intermediate (*N) adsorption on CuO (111) nanobelts (left panel) and the free energy diagrams illustrating the reaction pathways for NH3 formation through NtrRR (right). Reproduced with permission[46]. Copyright 2021, Wiley Online Library. XANES: X-ray absorption near edge structure; EXAFS: extended X-ray absorption fine structure.
Furthermore, Zhong et al. synthesized Cu2O with exposed (100), (111), and mixed (100) and (111) facets
Figure 6. Non-noble metal electrocatalysts with low-index facets for the NtrRR. (A) SEM images of the Cu2O with specific exposed facet (left panel) and the time-dependent in-situ FT-IR spectra: Cu2O (100) and (111) electrocatalyst at -1.2 V vs. Ag/AgCl in nitrate solution (middle and right). Reproduced with permission[47]. Copyright 2022, Elsevier; (B) Surface energy diagrams of Ni2P with different orientations. Reproduced with permission[48]. Copyright 2021, American Chemical Society; (C) The NtrRR free energy diagram of
In addition to Cu, other transition metals have also been investigated. As a demonstration, Yao et al. synthesized Ni2P with the exposed (111) facet on a Ni foam as a self-supported electrocatalyst for the NtrRR, which achieved an NH3 yield of up to 0.056 mmol·h-1·mg-1 and a Faraday efficiency of up to 99.23%[48]. They found that the Ni2P (111) can promote the water dissociation and generate active hydrogen atom *H, which then induced the *H-mediated reaction pathway and thus achieved a high NH3 selectivity. DFT calculations further revealed that among Ni2P (111), (201), (210), and (211), the (111) facet possesses the minimal surface energy and is stable in a real environment [Figure 6B], and NO3- is more likely to be adsorbed on the
Composite electrocatalysts with noble and non-noble metals
It should be noted that in most cases, the NtrRR performance of non-noble electrocatalysts is still inferior to that of noble metals. On the other hand, noble metal electrocatalysts suffer from high cost. Therefore, researchers are exploring the potential of composite electrocatalysts with noble and non-noble metals, aiming to achieve an optimal balance of both the activity and cost.
Zhang et al. designed an Au1Cu (111) single-atom alloy (SAA) with Cu vacancies on the surface (VCu Au1Cu SAA) [Figure 6D][50], which exhibited an NH3 Faraday efficiency of up to 98.7% and an NH3 yield of
ELECTROCATALYSTS WITH SPECIFIC HIGH-INDEX FACETS FOR THE NtrRR
High-index facets, in contrast to low-index facets, have a higher concentration of low coordination atoms, such as steps and twist sites. Consequently, these high-index facets often demonstrate enhanced electrocatalytic performance. The application of crystal facets as model catalysts in fundamental studies has shown that high-index facet-centered cubic (FCC) metals, such as Pt, Pd, Ir, Au, Ag, Cu, and Ni, exhibit remarkable catalytic activity for a wide range of chemical reactions, including the NtrRR. For example, Chen et al. synthesized tetrahedral Cu nanocrystals with exposed (520) high-index [THH Cu(520)] facets using an electrochemical square wave potential method without additional capping agents [Figure 7A][52]. The catalyst exhibited excellent NtrRR performance. In a neutral solution, at a potential of -0.90 V vs. RHE, the Faraday efficiency was as high as 98.3%, and the NH3 yield was as high as 9.13 mmol·h-1·cm-2. This performance significantly surpassed that of Cu nanocrystals with exposed (100) and (111) low-index facets. By adjusting the adsorption strength of intermediates through alloying, the electrocatalytic activity can be further improved. Liu et al. synthesized concave octahedral TOH Au-Pd alloy nanocrystals with exposed (331) high-index facets using the electrochemical double-step potential method [Figure 7B][53]. The results indicated that due to the low coordination number of high-index facets and the electronic interactions of Au-Pd alloys, the concave TOH Au-Pd alloy nanoparticles exhibit excellent NtrRR activity and selectivity compared with Au (311) and (111) facets [Figure 7C]. Remarkably, under ambient conditions, the highest NH3 yield of 4,591.71 μg·h-1·mgcat-1 and the Faraday efficiency was 62% was achieved at a potential of -1.15 V vs. saturated calomel electrode (SCE). DFT calculations indicated that the Pd-modified Au (331) step surface endows high activity for NO3- adsorption and N–O bond cleavage, enhancing the activity and selectivity of NtrRR. Although high-index facets show promising NtrRR performance, their synthesis is generally much more challenging, and thus, electrocatalysts with high-index facets have considerably less been investigated for NtrRR.
Figure 7. Electrocatalysts with high-index facets for the NtrRR. (A) TEM image, SAED pattern of a THH Cu NC (left panel), atomic model of (520) facet (middle), and Faraday efficiencies of various Cu catalysts (right). Reproduced with permission[52]. Copyright 2022, Elsevier; (B) SEM image, TEM image, and the corresponding SAED patterns of concave TOH Au–Pd NCs (left panel), optimized structures of intermediates of *NO3-, *NO2- + *O, *NO2- and *NO + *O (middle), and free energy profiles for NtrRR on Au (111) and (331), and TOH Au–Pd NCs (right). Reproduced with permission[53]. Copyright 2023, American Chemical Society; (C) Faraday efficiencies of main products at different working potentials of TOH Au–Pd NCs (left panel), NH3 yield rate and Faraday efficiencies of Au (111), Au (331), and TOH Au–Pd NCs (middle), and FE of main products of Au (111), Au (331), and TOH Au–Pd NCs at -1.15 V vs SCE (right). Reproduced with permission[53]. Copyright 2023, American Chemical Society. TEM: Transmission electron microscopy; SAED: selected area electron diffraction; THH: tetrahexahedron; NC: nanocrystals; SEM: scanning electron microscope; TOH: trisoctahedron; FE: Faraday efficiency; SCE: saturated calomel electrode.
CONCLUSIONS AND PERSPECTIVES
Over the past few years, significant strides have been made in exploring efficient electrocatalysts in terms of crystal facet engineering for nitrate reduction to ammonia, from low-index to high-index facets, from single metals to alloys and further more complex composites. The current review summarizes the current progress in crystal facets engineering of NtrRR electrocatalysts [Table 1].
Key performance parameters of low-index and high-index facets electrocatalysts in the NtrRR
Catalyst | Specific crystal facet | Synthetic method | Electrolyte | NH3 faradaic efficiency | NH3 yield rate | Authors |
Pd | (111) | Wet-synthesis | 0.1 M Na2SO4 and 0.1 M KNO3 | 79.91% | 2.74 mmol·h-1·mg-1 | Han et al.[38] |
Rh | (111) | 95% | 0.8 μg·h-1·cm-2 | Liu et al.[41] | ||
Pd | (111), (100) | 0.1 M NaOH and 20 mM NaNO3 | 35% | 307 μg·h-1·mg-1 | Lim et al.[39] | |
Cu | (100), (111) | 1 M KOH and 0.2 M KNO3 | 88% | 1.41 mmol·h-1·cm-2 | Fu et al.[45] | |
Cu2O | (111) | 0.5 M Na2SO4 and 100 ppm NaNO3 | 97.59% | 0.075 mmol·mgcat-1·h-1 | Zhong et al.[47] | |
VCu Au1Cu SAA | Cu (111) | 0.1 M KOH and 7.14 mM NO3- | 98.7% | 555 μg·h-1·cm-2 | Zhang et al.[50] | |
Au/Cu SAAs | Cu (100) | 0.5 M Na2SO4 and 100 ppm NaNO3 | 99.69% | 0.193 mmol·h-1·cm-2 | Yin et al.[51] | |
Cu | (111), (100) | Near-neutral and alkaline strong acidic | - | - | Hu et al.[44] | |
Rh | (100) | Alkaline | 20.8% | 34.4 μg·h-1·cm-2 | Guo et al.[40] | |
Cu | (100) | Electrosynthesis | 1 M KOH and 0.1 M KNO3 | 95.3% | 650 mmol·gcat-1·h-1 | Hu et al.[46] |
Cu | (520) | 100 mM K2SO4 and 100 mM KNO3 | 98.3% | 9.13 mmol·h-1·cm-2 | Chen et al.[52] | |
Au-Pd | Au (331) | 0.5 M K2SO4 and 0.05 M KNO3 | 61.96% | 4,591.71 μg·h-1·mgcat-1 | Liu et al.[53] | |
Pt | (111) | Solid-state synthesis | Acidic | - | - | Molodkina et al.[43] |
Ni2P | (111) | 0.5 M Na2SO4 and 80 mg·L-1 NaNO3 | 99.23% | 0.056 mmol·h-1·mg-1 | Yao et al.[48] | |
In3Sn | (100) | - | - | - | Yin et al.[17] |
The facet-engineered catalysts can not only provide more active and selective sites for the NtrRR by tuning the adsorption and activation energies of the reactants and intermediates but also modulate the electron transfer and mass transport processes. In addition, crystal facet engineering can be combined with other strategies, such as doping, alloying, heterostructuring, and defect engineering, to further improve the NtrRR performance. Despite the great progress, many challenges yet also great opportunities persist in this field.
(1) The synthesis of electrocatalysts with specific crystal facets, particularly high-index facets, is often quite challenging and requires precise control and advanced techniques. Currently, most of the reported catalysts with high-index facets crystallize in a simple cubic crystal system, while more complex compounds such as oxides have considerably less been explored. Therefore, more efficient and reliable methods for synthesizing and characterizing the facet-engineered catalysts with high quality and reproducibility need to be developed.
(2) The stability and durability of the facet-engineered catalysts are often compromised by the surface reconstruction, aggregation, and dissolution under harsh reaction conditions. Indeed, self-reconfiguration induced by potential is a frequently observed phenomenon in electrocatalysis. This is particularly true during the anodic oxidation process, which can lead to substantial alterations in the composition and structure of electrocatalysts. While catalyst reconstruction during the cathodic reduction process is relatively uncommon, studies still indicate that such a process can occur. For example, Li et al. discovered that the NiCu bimetallic hydroxide (NiCu-OH) catalyst rapidly converts into a composite of crystalline metallic copper (c-Cu) and amorphous nickel hydroxide [a-Ni(OH)2] during the NtrRR[54]. The reconstruction not only alters the material composition but also changes the crystal facet exposed by the catalyst. It transitions from the Cu2(OH)3(NO3)-exposed (121) facet to the Cu-exposed (111) facet. In this case, the engineered facets might not be the real active sites, and thus, the role of crystal facets in the NtrRR electrocatalysis needs to be carefully evaluated. Real-time monitoring of the surface facet evolution is, therefore, essential to reveal the detailed electrocatalytic reaction mechanism on specific facets.
(3) NtrRR is a complex multi-step process involving various intermediates and pathways, and the reaction mechanism is still not fully understood. In this case, how the crystal facets affect the reaction mechanism requires further investigation. In addition, there is a current absence of standardized criteria for evaluating the performance of NtrRR. Various reported catalysts were tested under different conditions (e.g., the type and concentration of the supporting electrolyte, applied potential, and cumulative ammonia production time). This brings additional difficulty in comparing the activity of reported catalysts with specific exposed facets. In this regard, the reaction conditions and parameters, such as temperature, pressure, pH, electrolyte, and potential, should be optimized, while the criteria for performance evaluation should be standardized to fairly compare the performance of different reported catalysts.
(4) The NtrRR competes with the HER on most metal surfaces. Crystal facet engineering might simultaneously promote both the NtrRR and HER. Exploring specific facets with high activity and selectivity is essential for achieving a high Faraday efficiency and selectivity towards the production of NH3.
(5) Further research, both experimental and theoretical, should be conducted to explore the relationship between the crystal facet structure and the NtrRR performance. Using in situ or operational characterization techniques is essential to obtain a comprehensive understanding of the dynamic structure, activity, selectivity, and stability of catalysts. These methods enable the investigation of catalytic processes and reaction mechanisms at the atomic and molecular levels. Based on these understandings, together with the big data and artificial intelligence, the discovery of high-performance NtrRR electrocatalysts with specific exposed crystal facets can be greatly facilitated.
(6) Currently, the crystal facet engineering of the electrocatalysts mainly focuses on improving the activity and stability. Further integrating the facet-engineered catalysts with other components, such as electrodes, membranes, and reactors, is also important to achieve scalable and practical applications of the NtrRR, and there could be many engineering issues. For example, determining how to expose the specific crystal facets of the catalysts during the electrode fabrication process often involves using binders and conductive additives that could block the exposed surface.
Overall, we believe that crystal facet engineering could play a significant role in enhancing the NtrRR performance of electrocatalysts. Through this review, we hope that the readers would gain better understanding of the impacts of crystal facets on the NtrRR reaction pathway, kinetics, and thermodynamics and could find useful information for designing high-performance electrocatalysts with specific exposed facets.
DECLARATIONS
Authors’ contributions
Proposed the topic of this review: Liang H
Prepared the manuscript: Zhang Y
Collectively discussed and revised the manuscript: Zhang Y, Liang H
Availability of data and materials
Not applicable.
Financial support and sponsorship
This work was supported by the Fundamental Research Funds for the Central Universities of China (Grant No. 20720210010).
Conflicts of interest
Liang H is the guest editor of the Special Issue “Energy Storage and Conversion Based on Metal-Organic Frameworks”, while the other author has declared that he has no conflicts of interest.
Ethical approval and consent to participate
Not applicable.
Consent for publication
Not applicable.
Copyright
© The Author(s) 2024.
REFERENCES
1. Foster SL, Bakovic SIP, Duda RD, et al. Catalysts for nitrogen reduction to ammonia. Nat Catal 2018;1:490-500.
2. Kyriakou V, Garagounis I, Vourros A, Vasileiou E, Stoukides M. An electrochemical Haber-Bosch process. Joule 2020;4:142-58.
3. Chang F, Gao W, Guo J, Chen P. Emerging materials and methods toward ammonia-based energy storage and conversion. Adv Mater 2021;33:e2005721.
4. Valera-Medina A, Xiao H, Owen-Jones M, David W, Bowen P. Ammonia for power. Prog Energ Combust 2018;69:63-102.
5. Soloveichik G. Electrochemical synthesis of ammonia as a potential alternative to the Haber-Bosch process. Nat Catal 2019;2:377-80.
6. Smith C, Hill AK, Torrente-murciano L. Current and future role of Haber-Bosch ammonia in a carbon-free energy landscape. Energy Environ Sci 2020;13:331-44.
7. Zhu W, Yao F, Wu Q, et al. Weakened d–p orbital hybridization in in situ reconstructed Ru/β-Co(OH)2 heterointerfaces for accelerated ammonia electrosynthesis from nitrates. Energy Environ Sci 2023;16:2483-93.
8. Ren Y, Yu C, Tan X, et al. Strategies to activate inert nitrogen molecules for efficient ammonia electrosynthesis: current status, challenges, and perspectives. Energy Environ Sci 2022;15:2776-805.
9. Macfarlane DR, Cherepanov PV, Choi J, et al. A roadmap to the ammonia economy. Joule 2020;4:1186-205.
10. Zhang F, Luo J, Chen J, et al. Interfacial assembly of nanocrystals on nanofibers with strong interaction for electrocatalytic nitrate reduction. Angew Chem Int Ed Engl 2023;62:e202310383.
11. Wang J, Feng T, Chen J, et al. Electrocatalytic nitrate/nitrite reduction to ammonia synthesis using metal nanocatalysts and bio-inspired metalloenzymes. Nano Energy 2021;86:106088.
12. Wu Z, Song Y, Liu Y, Luo W, Li W, Yang J. Electrocatalytic nitrate reduction: selectivity at the crossroads between ammonia and nitrogen. Chem Catal 2023;3:100786.
13. Zhu W, Zhang X, Yao F, et al. A hydrazine-nitrate flow battery catalyzed by a bimetallic RuCo precatalyst for wastewater purification along with simultaneous generation of ammonia and electricity. Angew Chem Int Ed Engl 2023;62:e202300390.
14. Wang Z, Liu S, Zhao X, et al. Interfacial defect engineering triggered by single atom doping for highly efficient electrocatalytic nitrate reduction to ammonia. ACS Mater Lett 2023;5:1018-26.
15. Sun N, Guo Y, Luo L, Cai X, Shen S, Zhang J. Facile synthesis of CuCo-CoO composite electrocatalyst for nitrate reduction to ammonia with high activity, selectivity and stability. Appl Surf Sci 2023;624:157118.
16. Bai Z, Li X, Ding L, Qu Y, Chang X. Artificial Cu-Ni catalyst towards highly efficient nitrate-to-ammonia conversion. Sci China Mater 2023;66:2329-38.
17. Yin H, Mao X, Bell S, Golberg D, Du A. Transition-metal-free, pure p-block alloy electrocatalysts for the highly efficient nitrate reduction to ammonia. Chem Mater 2023;35:2884-91.
18. Zhang Z, Liu Y, Su X, et al. Electro-triggered Joule heating method to synthesize single-phase CuNi nano-alloy catalyst for efficient electrocatalytic nitrate reduction toward ammonia. Nano Res 2023;16:6632-41.
19. Xiao C, Lu B, Xue P, et al. High-index-facet- and high-surface-energy nanocrystals of metals and metal oxides as highly efficient catalysts. Joule 2020;4:2562-98.
20. Li Y, Li M, Li S, Liu Y, Chen J, Wang Y. A review of energy and environment electrocatalysis based on high-index faceted nanocrystals. Rare Met 2021;40:3406-41.
21. Feng S, Li D, Dong H, et al. Tailoring the Mo-N/Mo-O configuration in MoO2/Mo2N heterostructure for ampere-level current density hydrogen production. Appl Catal B Environ 2024;342:123451.
22. de Groot M, Koper M. The influence of nitrate concentration and acidity on the electrocatalytic reduction of nitrate on platinum. J Electroanal Chem 2004;562:81-94.
23. Xu B, Li D, Zhao Q, Feng S, Peng X, Chu PK. Electrochemical reduction of nitrate to ammonia using non-precious metal-based catalysts. Coord Chem Rev 2024;502:215609.
24. Gao J, Jiang B, Ni C, Qi Y, Bi X. Enhanced reduction of nitrate by noble metal-free electrocatalysis on P doped three-dimensional Co3O4 cathode: mechanism exploration from both experimental and DFT studies. Chem Eng J 2020;382:123034.
25. Tong W, Huang B, Wang P, Shao Q, Huang X. Exposed facet-controlled N2 electroreduction on distinct Pt3Fe nanostructures of nanocubes, nanorods and nanowires. Natl Sci Rev 2021;8:nwaa088.
26. Tan L, Yang N, Huang X, et al. Synthesis of ammonia via electrochemical nitrogen reduction on high-index faceted Au nanoparticles with a high faradaic efficiency. Chem Commun 2019;55:14482-5.
27. Bao D, Zhang Q, Meng FL, et al. Electrochemical reduction of N2 under ambient conditions for artificial N2 fixation and renewable energy storage using N2/NH3 cycle. Adv Mater 2017;29:1604799.
28. Yu Y, Zhang Q, Liu B, Lee JY. Synthesis of nanocrystals with variable high-index Pd facets through the controlled heteroepitaxial growth of trisoctahedral Au templates. J Am Chem Soc 2010;132:18258-65.
29. Sun S, Zhang X, Cui J, Yang Q, Liang S. High-index faceted metal oxide micro-/nanostructures: a review on their characterization, synthesis and applications. Nanoscale 2019;11:15739-62.
30. Rosen J, Hutchings GS, Lu Q, et al. Mechanistic insights into the electrochemical reduction of CO2 to CO on nanostructured Ag surfaces. ACS Catal 2015;5:4293-9.
31. Dong JC, Su M, Briega-Martos V, et al. Direct in situ raman spectroscopic evidence of oxygen reduction reaction intermediates at high-index Pt(hkl) surfaces. J Am Chem Soc 2020;142:715-9.
32. Yin Y, Alivisatos AP. Colloidal nanocrystal synthesis and the organic-inorganic interface. Nature 2005;437:664-70.
33. Yang Y, Zhang J, Wei Y, et al. Solvent-dependent evolution of cyclic penta-twinned rhodium icosahedral nanocrystals and their enhanced catalytic properties. Nano Res 2018;11:656-64.
34. Liang H, Jiang X, Qi Z, et al. Hematite concave nanocubes and their superior catalytic activity for low temperature CO oxidation. Nanoscale 2014;6:7199-203.
35. Liang Y, Shang L, Bian T, et al. Shape-controlled synthesis of polyhedral 50-facet Cu2O microcrystals with high-index facets. CrystEngComm 2012;14:4431-6.
36. Hu S, Tian N, Li M, et al. Trapezohedral platinum nanocrystals with high-index facets for high-performance hydrazine electrooxidation. Chem Synth 2023;3:4.
37. Huang L, Liu M, Lin H, et al. Shape regulation of high-index facet nanoparticles by dealloying. Science 2019;365:1159-63.
38. Han Y, Zhang X, Cai W, et al. Facet-controlled palladium nanocrystalline for enhanced nitrate reduction towards ammonia. J Colloid Interface Sci 2021;600:620-8.
39. Lim J, Liu C, Park J, et al. Structure sensitivity of Pd facets for enhanced electrochemical nitrate reduction to ammonia. ACS Catal 2021;11:7568-77.
40. Guo Y, Cai X, Shen S, Wang G, Zhang J. Computational prediction and experimental evaluation of nitrate reduction to ammonia on rhodium. J Catal 2021;402:1-9.
41. Liu H, Timoshenko J, Bai L, et al. Low-coordination rhodium catalysts for an efficient electrochemical nitrate reduction to ammonia. ACS Catal 2023;13:1513-21.
42. Katsounaros I, Figueiredo MC, Chen X, Calle-vallejo F, Koper MT. Interconversions of nitrogen-containing species on Pt(100) and Pt(111) electrodes in acidic solutions containing nitrate. Electrochimica Acta 2018;271:77-83.
43. Molodkina EB, Botryakova IG, Rudnev AV, Ehrenburg MR. Redox-transitions in NO/NH3 adlayers on a Pt(111) electrode in an acidic solution. Electrochimica Acta 2023;444:141997.
44. Hu T, Wang C, Wang M, Li CM, Guo C. Theoretical insights into superior nitrate reduction to ammonia performance of copper catalysts. ACS Catal 2021;11:14417-27.
45. Fu Y, Wang S, Wang Y, et al. Enhancing electrochemical nitrate reduction to ammonia over Cu nanosheets via facet tandem catalysis. Angew Chem Int Ed Engl 2023;62:e202303327.
46. Hu Q, Qin Y, Wang X, et al. Reaction intermediate-mediated electrocatalyst synthesis favors specified facet and defect exposure for efficient nitrate–ammonia conversion. Energy Environ Sci 2021;14:4989-97.
47. Zhong W, Gong Z, He Z, et al. Modulating surface oxygen species via facet engineering for efficient conversion of nitrate to ammonia. J Energy Chem 2023;78:211-21.
48. Yao Q, Chen J, Xiao S, Zhang Y, Zhou X. Selective electrocatalytic reduction of nitrate to ammonia with nickel phosphide. ACS Appl Mater Interfaces 2021;13:30458-67.
49. Crawford J, Yin H, Du A, O’Mullane AP. Nitrate-to-ammonia conversion at an InSn-enriched liquid-metal electrode. Angew Chem Int Ed Engl 2022;61:e202201604.
50. Zhang Y, Chen X, Wang W, Yin L, Crittenden JC. Electrocatalytic nitrate reduction to ammonia on defective Au1Cu (111) single-atom alloys. Appl Catal B Environ 2022;310:121346.
51. Yin H, Peng Y, Li J. Electrocatalytic reduction of nitrate to ammonia via a Au/Cu single atom alloy catalyst. Environ Sci Technol 2023;57:3134-44.
52. Chen L, Xie A, Lou Y, Tian N, Zhou Z, Sun S. Electrochemical synthesis of tetrahexahedral Cu nanocrystals with high-index facets for efficient nitrate electroreduction. J Electroanal Chem 2022;907:116022.
53. Liu F, Chen C, Jiang X, et al. High-index surface structure engineering of Au–Pd concave triple-octahedrons for boosting electrocatalytic nitrate reduction to ammonia. ACS Sustain Chem Eng 2023;11:1631-7.
Cite This Article
Export citation file: BibTeX | EndNote | RIS
OAE Style
Zhang Y, Liang H. Crystal facet engineering of electrocatalysts for nitrate reduction to ammonia: recent advances and future perspectives. Chem Synth 2024;4:39. http://dx.doi.org/10.20517/cs.2023.74
AMA Style
Zhang Y, Liang H. Crystal facet engineering of electrocatalysts for nitrate reduction to ammonia: recent advances and future perspectives. Chemical Synthesis. 2024; 4(3):39. http://dx.doi.org/10.20517/cs.2023.74
Chicago/Turabian Style
Zhang, Yuwei, and Hanfeng Liang. 2024. "Crystal facet engineering of electrocatalysts for nitrate reduction to ammonia: recent advances and future perspectives" Chemical Synthesis. 4, no.3: 39. http://dx.doi.org/10.20517/cs.2023.74
ACS Style
Zhang, Y.; Liang H. Crystal facet engineering of electrocatalysts for nitrate reduction to ammonia: recent advances and future perspectives. Chem. Synth. 2024, 4, 39. http://dx.doi.org/10.20517/cs.2023.74
About This Article
Copyright
Data & Comments
Data
![](https://g.oaes.cc/oae/nuxt/img/like.08d1ca4.png)
Comments
Comments must be written in English. Spam, offensive content, impersonation, and private information will not be permitted. If any comment is reported and identified as inappropriate content by OAE staff, the comment will be removed without notice. If you have any queries or need any help, please contact us at support@oaepublish.com.